Ultra-Low-Loss Silicon Nitride on Sapphire for Broad-Transparency Nonlinear and Quantum Photonics

Abstract:The field of photonic integrated circuits (PIC) has flourished in the past two decades, fueling numerous cutting-edge applications across sensing, networking, data interconnect, and quantum information processing. As a guiding material for PIC, Si$_3$N$_4$ has seen extensive use for its ultra-low loss, broad transparency, and diversity in implementation across both thin and thick films. Although the standard, traditional silicon dioxide (SiO$_2$) on silicon (Si) substrates that underpin the majority of Si$_3$N$_4$ photonics face drawbacks in the form of long-wavelength transparency limited by SiO$_2$, high-stress deposition for anomalous dispersion thick-film Si$_3$N$_4$, and leakage loss to the Si layer for low-confinement thin-film Si$_3$N$_4$. Featuring increased long-wavelength transparency into the mid-infrared, low-stress deposition of Si$_3$N$_4$, and a low index, this work investigates sapphire substrates as alternate hosts for Si$_3$N$_4$ photonics with greater spectral coverage and reduced fabrication complexity. This work presents a robust method of fabricating ultra-low loss photonic integrated circuits on a 500-nm-thick Si$_3$N$_4$-on-sapphire platform, exhibiting record-low losses below $0.1 \rm \;dB/cm$. Implemented using this process are high-Q microrings with intrinsic quality factors in excess of $4.5\times10^6$ and coupled-ring photonic molecules to support nonlinear gain. Leveraging the achievable low loss and high-Q, this work further reports the first demonstration of Kerr-comb and soliton generation on the Si$_3$N$_4$-on-sapphire platform. These advances in loss, quality factor, and soliton generation on this versatile, broad-transparency platform pave the way for future work in spectroscopy and quantum-enhanced sensing across previously prohibited spectral regions for Si$_3$N$_4$ photonics with reduced fabrication complexity.

Optics (physics.optics); Quantum Physics (quant-ph)

arXiv:2608.27335 [physics.optics]

(or arXiv:2608.27335v1 [physics.optics] for this version)

https://doi.org/10.48550/arXiv.2608.27335 Focus to learn more arXiv-issued DOI via DataCite (pending registration)

arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.

Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.

Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.